XYMERTOL RAPID COLD CURE PRIMER

Xymertol Rapid Cold Cure Primer is an unpigmented, solvent free, two part polyurethane/ urea concrete primer that in cold conditions is ready to re-coat in 20 minutes down to a temperature 0°c, thanks to the use of Cold Cure Technology.

Xymertol Rapid Cold Cure Primer has a long pot life but when applied is quickly cured by the action of atmospheric moisture. It will quickly develop a bond to concrete that is stronger than the concrete itself.

Xymertol Rapid Cold Cure Primer  can be used for priming and sealing porosity in concrete, masonry and other non metallic substrates before coating with polyurea spray, polyurethane or epoxy coatings, mortars or screeds.

This product is ideal for cold storage facilities, for a primer for normal room temperature please see Xymertol Rapid Prime.

Conseal Prime

Type: Two part moisture activated polyurea coating 

Mix Ratio: See label on tin

Hardener: Xyanco 243 

Resin Density: 1.06kg/litre

Coverage: 7-10 m2/litre, depending on surface texture and porosity 

Minimum over-coating time: 20 minutes 

Maximum over-coating time: 48 hours 

Solvent: Thin with Xysol PU if necessary and for spraying

Colours: Clear 

Pack Sizes: 1, 2.5, 5 and 10 litres

Shelf life and Storage: 6-12 months in original, unopened container. Store in cool and dry conditions. ddd

Preperation:  Concrete substrates should preferably be diamond ground or blasted but if this is not possible the surface must be clean and free of loose material, laitance, oil, grease etc.

Mixing: Add all of the hardener to the tin of resin and mix slowly for several minutes preferably using a flat mixing blade in a drill. Try not to mix air in with the resin as this will reduce pot life. If you require a smaller quantity or are unable to use all of the material within its pot life, weigh out resin and hardener in the proportions specified on the label using digital scales.

Application: Can be applied by brush, roller or airless spray. A thin coat should be applied ensuring that the material is worked well into pin holes and imperfections so that 100% of the surface has been covered. Avoid leaving excess material to form thick areas as foaming may occur. On some porous substrates a second coat may be required to completely seal all porosity.

Over-coating: Can be overcoated with virtually all other types of coating as soon as it can be walked on which is 20-30 minutes in most conditions.

Advantages

  • Rapid Cure: Can usually be over-coated in 20 minutes
  • Cold Cure:  Will cure down to 0°c with Xymertec CCT Technology in 20-40 minutes
  • High Tensile Strength: Rapidly develops an exceptional bond to dry and slightly damp substrates
  • Easy to Apply: Easy to mix and apply
  • Long Pot Life: After mixing gives ample time for application
  • Compatible: Can, be over-coated with most other coatings including epoxy, polyurea, polyurethane, polyaspartic ect.